| Properties | Test Method | Test Condition | Units | Typical Values |
| Physical | ||||
| Melt Flow Rate | ISO1133 | 230ºC, 2.16Kg | g/10min | 58±2 |
| Specific Gravity | ISO1183 | 23ºC | g/cm3 | — |
| Ash | ISO3451 | 800ºC,30min | % | — |
| Mechanical | ||||
| Tensile Strength | ISO527 | 50mm/min | MPa | 24 |
| Elongation at Break | ISO527 | 50mm/min | % | 6 |
| Flexural Strength | ISO178 | 2mm/min | MPa | — |
| Flexural Modulus | ISO178 | 2mm/min | MPa | — |
| Impact Strength, IZOD non-notched | ISO179 | 23ºC | KJ/m2 | NB |
| -30ºC | KJ/m2 | – | ||
| Impact Strength, IZOD notched | ISO179 | 23ºC | KJ/m2 | – |
| -30ºC | KJ/m2 | – | ||
| Thermal | ||||
| Heat Deflection Temp. | ISO75 | 0.45MPa | ºC | 95 |
| 1.8MPa | ºC | – | ||
| (Melting Point) | DSC | ºC | ||
| Others | ||||
| Hardness | ISO2039 | – | N/mm2 | |
| Mold Shrinkage | – | 23ºC | ||
| Flammability | TL1010 | – | mm/min | |